| Stress relieved | |||||
| Stress Relieved Temperature | Stress Relieved Testing Time | 保護(hù)氣體 | 屈服強(qiáng)度 | 延伸率 | 抗拉強(qiáng)度 |
| 760 °C | 2 hr | Ar (I1) EN | 690 MPa | 20 % | 785 MPa |
| 760 °C | 2 hr | Ar (I1) EN | 420 MPa | 22 % | 450 MPa |
| 760 °C | 2 hr | Ar (I1) EN | 500 MPa | 16 % | 560 MPa |
| 760 °C | 2 hr | Ar (I1) EN | 510 MPa | 14 % | 580 MPa |
| 735 °C | 4 hr | Ar (I1) EN | 670 MPa | 20 % | 760 MPa |
| Stress relieved | ||||
| Stress Relieved Testing Temp | Stress Relieved Testing Time | 保護(hù)氣體 | 沖擊值 | 測(cè)試溫度 |
| 760 °C | 2 hr | Ar (I1) EN | 200 J | 20 °C |
| 760 °C | 2 hr | Ar (I1) EN | 180 J | 0 °C |
| 760 °C | 2 hr | Ar (I1) EN | 150 J | -20 °C |
| 760 °C | 2 hr | Ar (I1) EN | 90 J | -40 °C |
| 760 °C | 2 hr | Ar (I1) EN | 70 J | -60 °C |
| 735 °C | 4 hr | Ar (I1) EN | 210 J | 20 °C |
| 735 °C | 4 hr | Ar (I1) EN | 190 J | 0 °C |
| 735 °C | 4 hr | Ar (I1) EN | 130 J | -20 °C |
| 735 °C | 4 hr | Ar (I1) EN | 60 J | -40 °C |
| 735 °C | 4 hr | Ar (I1) EN | 30 J | -60 °C |
| Mn | Mo | C | Si | V | Ni | N | Cr |
| 0.5 % | 0.9 % | 0.1 % | 0.3 % | 0.20 % | 0.5 % | 8.7 % |
| 認(rèn)證: | 2.0MM, NAKS/HAKC, 07686, VdTüV |
| 分類(lèi): | W CrMo91, EN ISO 21952-A, Wire Electrode, W 62 9C1MV, EN ISO 21952-B, Wire Electrode, ER90S-B9, SFA/AWS A5.28, Wire Electrode |
認(rèn)證均基于工廠的所在地。如需更多信息，請(qǐng)聯(lián)系伊薩。
| 合金類(lèi)型: | Alloyed steel (9 % Cr - 1 % Mo - V - N) "9CrMoVN" |
OK Tigrod 13.38是一種適用于高溫鋼和煉油廠熱氫環(huán)境用鋼GTAW焊接的無(wú)鍍銅低合金9CrMoVN焊絲。該焊絲適合用于諸如P 91/T 91鋼等9% Cr鋼種。 該合金的雜質(zhì)元素限值已經(jīng)過(guò)修改，因此極其“純凈”。其在室溫和高溫條件下均可獲得較高強(qiáng)度。 AWS已對(duì)該產(chǎn)品的歸類(lèi)進(jìn)行修改。此前歸類(lèi)編號(hào)為A5.9 ER505。