| As welded | |||
| 保護(hù)氣體 | 屈服強(qiáng)度 | 延伸率 | 抗拉強(qiáng)度 |
| ISO | 410 MPa | 35 % | 590 MPa |
| AWS | - | - | - |
| As welded | ||
| 保護(hù)氣體 | 沖擊值 | 測試溫度 |
| ISO | 80 J | 20 °C |
| ISO | 70 J | -140 °C |
| Mn | Mo | Cu | C | Si | Ferrite FN | Ni | N | Cr |
| 1.0 % | 4.8 % | 1.70 % | 0.03 % | 0.5 % | 0 % | 25.5 % | 20.5 % |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 44 sec | 0.60 kg | 91 | 60-85 A | 0.9 kg/h | 24 V | 2.5 x 300 mm |
| 60 sec | 0.58 kg | 41 | 85-130 A | 1.5 kg/h | 27 V | 3.2 x 350 mm |
| 64 sec | 0.51 kg | 30 | 95-180 A | 1.9 kg/h | 29 V | 4.0 x 350 mm |
| 認(rèn)證: | EN 13479, CE, UNA 272580, Seproz, 02723, VdTüV |
| 分類: | E 20 25 5 Cu N L R 3 2, EN ISO 3581-A, E385-16, SFA/AWS A5.4, 1.4519, Werkstoffnummer |
認(rèn)證均基于工廠的所在地。如需更多信息，請聯(lián)系伊薩。
| Coating Type: | Basic Rutile |
| Ferrite Content: | FN 0 |
| Welding Current: | AC, DC+ |
| 合金類型: | Austenitic CrNi |