| As welded | |||
| 保護氣體 | 屈服強度 | 延伸率 | 抗拉強度 |
| ISO | 450 MPa | 35 % | 650 MPa |
| As welded | ||
| 保護氣體 | 沖擊值 | 測試溫度 |
| ISO | 90 J | 20 °C |
| ISO | 50 J | -196 °C |
| Mn | Mo | C | Si | Ferrite FN | Ni | N | Cr |
| 6.5 % | 3.0 % | 0.04 % | 0.5 % | 0 % | 16.0 % | 19.0 % |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 72 sec | 0.62 kg | 46 | 70-100 A | 1.2 kg/h | 24 V | 3.2 x 350 mm |
| 74 sec | 0.64 kg | 29 | 100-140 A | 1.8 kg/h | 25 V | 4.0 x 350 mm |
| 分類: | E 20 16 3 Mn N L B 4 2, EN ISO 3581-A, E316LMn-15, SFA/AWS A5.4, 1.4455, Werkstoffnummer |
| Coating Type: | Basic |
| Ferrite Content: | FN <0.5 |
| Welding Current: | DC+ |
| 合金類型: | CrNiMo |