| As welded | |||
| 保護(hù)氣體 | 屈服強(qiáng)度 | 延伸率 | 抗拉強(qiáng)度 |
| ISO | 700 MPa | 28 % | 900 MPa |
| As welded | ||
| 保護(hù)氣體 | 沖擊值 | 測試溫度 |
| ISO | 90 J | 20 °C |
| ISO | 70 J | -20 °C |
| ISO | 55 J | -40 °C |
| ISO | 45 J | -60 °C |
| Mn | Mo | C | Si | Ferrite FN | Ni | N | Cr |
| 0.9 % | 4.3 % | 0.03 % | 0.6 % | 45 % | 10.4 % | 25.2 % |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 48 sec | 0.62 kg | 93 | 50-80 A | 0.8 kg/h | 23 V | 2.5 x 300 mm |
| 68 sec | 0.63 kg | 46 | 60-100 A | 1.1 kg/h | 23 V | 3.2 x 350 mm |
| 70 sec | 0.62 kg | 32 | 100-140 A | 1.6 kg/h | 23 V | 4.0 x 350 mm |
| 認(rèn)證: | Duplex, DNV-GL |
| 分類: | E 25 9 4 N L B 4 2, EN ISO 3581-A, E2594-15, SFA/AWS A5.4, (1.4410), Werkstoffnummer |
認(rèn)證均基于工廠的所在地。如需更多信息，請聯(lián)系伊薩。
| Coating Type: | Basic |
| Ferrite Content: | FN 35-50 |
| Welding Current: | DC+ |
| 合金類型: | Austenitic CrNiMo |