| PWHT 600°C 8h | |||||
| 保護(hù)氣體 | 屈服強(qiáng)度 | 延伸率 | 抗拉強(qiáng)度 | Stress Relieved Temperature | Stress Relieved Testing Time |
| ISO | 680 MPa | 17 % | 900 MPa | - | - |
| Stress relieved | |||||
| 保護(hù)氣體 | 屈服強(qiáng)度 | 延伸率 | 抗拉強(qiáng)度 | Stress Relieved Temperature | Stress Relieved Testing Time |
| AWS | - | - | - | 600 °C | 1 hr |
| PWHT 600°C 8h | ||
| 保護(hù)氣體 | 沖擊值 | 測(cè)試溫度 |
| ISO | 65 J | 20 °C |
| ISO | 60 J | 0 °C |
| ISO | 55 J | -20 °C |
| Mn | Mo | C | Si | Ni | Cr |
| 0.6 % | 0.6 % | 0.04 % | 0.4 % | 4.5 % | 12.2 % |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 63 sec | 0.64 kg | 35 | 90-150 A | 1.6 kg/h | 28 V | 3.2 x 450 mm |
| 73 sec | 0.66 kg | 22 | 110-190 A | 2.2 kg/h | 28 V | 4.0 x 450 mm |
| 86 sec | 0.67 kg | 14 | 140-250 A | 3.1 kg/h | 27 V | 5.0 x 450 mm |
| 認(rèn)證: | UNA 272580, Seproz |
| 分類: | E Fe7, EN 14700, E 13 4 B 4 2, EN ISO 3581-A, E410NiMo-15, SFA/AWS A5.4, 1.4351, Werkstoffnummer |
認(rèn)證均基于工廠的所在地。如需更多信息，請(qǐng)聯(lián)系伊薩。
| Coating Type: | Basic |
| Diffusible Hydrogen: | <5.0 ml/100g |
| Welding Current: | DC+ |
| 合金類型: | Martensitic-ferritic |