| Stress relieved | |||||
| Stress Relieved Temperature | Stress Relieved Testing Time | 保護(hù)氣體 | 屈服強(qiáng)度 | 延伸率 | 抗拉強(qiáng)度 |
| 600 °C | 8 hr | ISO | 650 MPa | 17 % | 870 MPa |
| 600 °C | 2 hr | ISO | - | - | - |
| 600 °C | 1 hr | AWS | - | - | - |
| Stress relieved | ||||
| Stress Relieved Testing Temp | Stress Relieved Testing Time | 保護(hù)氣體 | 沖擊值 | 測試溫度 |
| 600 °C | 8 hr | ISO | 45 J | 20 °C |
| 600 °C | 8 hr | ISO | 45 J | -10 °C |
| 600 °C | 8 hr | ISO | 40 J | -40 °C |
| Mn | Mo | C | Si | Ni | Cr |
| 0.6 % | 0.6 % | 0.02 % | 0.4 % | 4.6 % | 12.0 % |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 61 sec | 0.62 kg | 73 | 55-100 A | 0.8 kg/h | 21 V | 2.5 x 350 mm |
| 66 sec | 0.59 kg | 45 | 65-135 A | 1.2 kg/h | 21 V | 3.2 x 350 mm |
| 92 sec | 0.59 kg | 23 | 90-190 A | 1.7 kg/h | 24 V | 4.0 x 450 mm |
| 認(rèn)證: | UNA 272580, Seproz |
| 分類: | E Fe7, EN 14700, E 13 4 R 3 2, EN ISO 3581-A, E410NiMo-16, SFA/AWS A5.4, 1.4351, Werkstoffnummer |
認(rèn)證均基于工廠的所在地。如需更多信息，請聯(lián)系伊薩。
| Coating Type: | Rutile Basic |
| Diffusible Hydrogen: | <8.0 ml/100g |
| Welding Current: | DC+, AC |
| 合金類型: | Martensitic 13Cr4Ni-Mo type |