| Stress relieved | |||||
| Stress Relieved Temperature | Stress Relieved Testing Time | 保護(hù)氣體 | 屈服強度 | 延伸率 | 抗拉強度 |
| 750 °C | 6 hr | AWS | - | - | - |
| 750 °C | 1 hr | AWS | 370 MPa | 25 % | 520 MPa |
| Stress relieved | ||||
| Stress Relieved Testing Temp | Stress Relieved Testing Time | 保護(hù)氣體 | 沖擊值 | 測試溫度 |
| 750 °C | 6 hr | AWS | 55 J | 20 °C |
| 750 °C | 6 hr | AWS | 35 J | 0 °C |
| 750 °C | 6 hr | AWS | 20 J | -20 °C |
| Mn | C | Si | Ni | Cr |
| 0.3 % | 0.04 % | 0.4 % | 0.1 % | 12.9 % |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 48 sec | 0.62 kg | 73 | 65-115 A | 1.0 kg/h | 25 V | 2.5 x 350 mm |
| 71 sec | 0.63 kg | 33 | 90-160 A | 1.5 kg/h | 25 V | 3.2 x 450 mm |
| 73 sec | 0.57 kg | 24 | 120-220 A | 2.0 kg/h | 30 V | 4.0 x 450 mm |
| 認(rèn)證: | UNA 272580, Seproz |
| 分類: | E Fe7, EN 14700, E 13 B 4 2, EN ISO 3581-A, E410-15, SFA/AWS A5.4, 1.4009, Werkstoffnummer |
認(rèn)證均基于工廠的所在地。如需更多信息，請聯(lián)系伊薩。
| Coating Type: | Lime Basic |
| Welding Current: | DC+ |
| 合金類型: | 13% Cr |