| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水率 | ASTM D-570 | >0.01 | % | |
| 熔體流動速率 | ASTM D-1238 | 19 | g/10min | ||
| 密度 | ASTM D-792 | 0.90 | g/cm3 | ||
| 機械性能 | 拉伸強度 | ASTM D-638 | 310 | kgf/cm2 | |
| 沖擊強度 | 帶缺口 | ASTM D-256 | 7 | kgf.cm/cm | |
| 彎曲模量 | ASTM D-790 | 11000 | kgf/cm2 | ||
| 線型成型收縮率 | KPIC Method | 1.0-2.0 | % | ||
| 洛氏硬度 | ASTM D-785 | 90 | scRale | ||
| 絕緣強度 | ASTM D-149 | 40 | KV/mm | ||
| 斷裂伸張率 | ASTM D-638 | <500 | % | ||
| 電氣性能 | 耐電弧性 | ASTM D-495 | 130 | sec. | |
| 介電常數(shù) | ASTM D-150 | 2.3 | |||
| 損耗因素 | ASTM D-150 | 2 | 10-4 | ||
| 體積電阻率 | ASTM D-257 | 1 | 1017ohm.cm | ||
| 熱性能 | 熔點 | ASTM D-3418 | 148 | ℃ | |
| 比熱容 | KPIC Method | 0.46 | cal/g℃ | ||
| 傳熱系數(shù) | KPIC Method | 3 | 10-4calcm/cmsec,℃ | ||
| 熱變形溫度 | ASTM D-648 | 90 | ℃ | ||